Antistatic Additive For PS

● PS 30AN is designed for HIPS resin.
● Addition level 10-22 wt% to achieve surface resitivity 10^7-10^11 Ohms/sq.
● Typical properties
– Melting Point 182°C
– Melt Flow Rate (200°C,2.16kg ) 14 g/10 min
– Surface Resistivity( 23°C, 50%R.H) 3.2×10E6 Ohms/sq

Share to:

Description

 

Antistatic Additive For PS2Introduction

Antistatic agent for plastic PS can be processed on conventional extrusion equipment ,to incorporate into PS polymer by certain dosage for target resistivity. Typically at low shear conditions. Actual processing temperatures should be adapted according to the nature of the equipment and the manufactured article to give optimal quality. More detailed information on processing conditions can be obtained from product data sheets.

    • Antistatic agent for plastic offer:
    • Flexibility in designing antistatic parts to the required performance level.
    • A single permanent antistatic agent for different polymer types, process types and applications,suitable for injection molding,sheet extrusion,film blown,coating.
    • Multiple dilutions of the concentrate possible, depending on resistivity level required,recmendded dosage 10%-22%.
    • Additional saving potential in overall raw material costs.

 

Highlights

Antistatic Additive For PS1

  • Is immediately functional and imparts long-term antistatic effect.
  • Effective under different humidity conditions,Is not migrating of the polymer.
  • Can easily be processed by extrusion and injection molding.
  • Suitable for any colour formulation, including clear and translucent formulation GPPS
  • Extremely effective to provide different performance targets (10^8-10^11 Ohm/sq.). Even results below 10^7 Ohms/sq.
  • antistatic agent for plastic are widely used in: injection molded ESD parts, transparent antistatic GPPS parts; PS films for electronic component packaging; ESD PS sheets and PS thermoforming trays.